Notch Effect in Polyetheretherketone (PEEK): Tensile and Fracture Tests - FRADDCO project

This dataset contains tensile and fracture tests of specimens made of polyetheretherketone (PEEK) material, manufactured by fused filament fabrication (FFF). The files include 9 tensile specimens and 60 single-edge-notch bending (SENB) specimens containing U-notches with different nominal notch radii (from 0 mm -crack-like defects- up to 2.0 mm) and fabricated with three different raster orientations: 0/90, 30/−60 and 45/−45.本数据集包含通过熔融沉积成型（fused filament fabrication，FFF）制备的聚醚醚酮（polyetheretherketone，PEEK）材料试样的拉伸与断裂试验数据。数据集文件涵盖9个拉伸试样，以及60个带有不同名义缺口半径（范围为0 mm——类裂纹缺陷——至2.0 mm）U型缺口的单边缺口弯曲（single-edge-notch bending，SENB）试样，上述试样均采用三种不同的铺丝取向制备：0/90、30/−60与45/−45。