Data for: Effect of Temperature on Electrochemical Pitting Corrosion Behavior of 316L Stainless Steel in MDEA Solution Containing Chloride

(1) Potentiodynamic polarization data of 316L SS in two solution at different temperatures: (a) plain MDEA solution (b) MDEA solution containing 1.0 wt % Cl−. (2)Breakdown potenital- temperature data for 316L SS in MDEA solution containing 1.0 wt % Cl−. (3)Potentiostatic polarization data of 316L SS at an anodic potential of 300 mV vs. Ag/AgCl (0.1 mol/L-1 KCl) in two solution at different temperatures and elapsed time: (a) plain MDEA solution (b) MDEA solution containing 1.0 wt % Cl−. (4)Data for EIS plots of the corrosion of 316L SS in plain MDEA amine solution at different temperatures: (a) Nyquist plot (b) impedance amplitude (c) phase angle. (5) Data for EIS plots of the corrosion of 316L SS in MDEA amine solution containing 1.0 wt% Cl− at different temperatures: (a) Nyquist plot (b) impedance amplitude (c) phase angle.

(1) 动电位极化（Potentiodynamic polarization）数据：316L不锈钢（316L SS）在两种不同温度的溶液中的动电位极化测试数据，分为(a) 空白甲基二乙醇胺（MDEA）溶液，(b) 含1.0 wt%氯离子（Cl−）的MDEA溶液。
(2) 316L不锈钢在含1.0 wt% Cl−的MDEA溶液中的击穿电位-温度关系数据。
(3) 恒电位极化（Potentiostatic polarization）数据：316L不锈钢在相对于以0.1 mol·L⁻¹ KCl为电解质的Ag/AgCl参比电极的300 mV阳极电位下，于两种溶液中、不同温度及不同时长下的恒电位极化测试数据，分为(a) 空白MDEA溶液，(b) 含1.0 wt% Cl−的MDEA溶液。
(4) 电化学阻抗谱（EIS, Electrochemical Impedance Spectroscopy）测试数据：316L不锈钢在空白MDEA胺溶液中、不同温度下的腐蚀电化学阻抗谱数据，分为(a) 奈奎斯特（Nyquist）图，(b) 阻抗模值，(c) 相位角。
(5) 316L不锈钢在含1.0 wt% Cl−的MDEA胺溶液中、不同温度下的腐蚀电化学阻抗谱数据，分为(a) 奈奎斯特图，(b) 阻抗模值，(c) 相位角。