Raw Data_Local fracture criterion H-assisted quasi-cleavage cracking tempered martensitic steels

Raw data to evaluate hydrogen-assisted cracking of three tempered martensitic steels (Ref -0.3C0.2Si0.4Mn1.0Cr0.8Mo, HMV-0.3C0.3Si0.3Mn0.5Cr-1.8Mo0.2V, HCV-0.6C0.3Si0.3Mn1.0Cr1.2Mo0.15V). It comprises: -Tensile tests: Unnotched and notched (Kt1.3, 1.5, 2.1, 4.2) round specimens: -> Air (without hydrogen) ->Hydrogen electrochemically pre-charged (20, 50 or 100 mA/cm2) and desorbed (30 minutes or 48 hours) Unnotched and notched (Kt1.1, 1.4, 3.2) flat specimens: -> Air (without hydrogen) ->Under electrochemically hydrogen permeation (5, 20 or 50 mA/cm2) -Electrochemical permeation: Stress free samples (5, 10, 20, 50 and 100 mA/cm2) Tensile loaded samples (5, 20 or 50 mA/cm2)用于评估三种回火马氏体钢氢致开裂行为的原始实验数据（参考钢种分别为Ref-0.3C0.2Si0.4Mn1.0Cr0.8Mo、HMV-0.3C0.3Si0.3Mn0.5Cr-1.8Mo0.2V以及HCV-0.6C0.3Si0.3Mn1.0Cr1.2Mo0.15V）。本数据集包含以下内容： - 拉伸试验： 分为无缺口与缺口（应力集中系数Kt分别为1.3、1.5、2.1、4.2）的圆形试样，测试工况包括： -> 空气环境（无氢氛围） -> 电化学预充氢（充氢电流密度分别为20、50或100 mA/cm²）并经解吸处理（解吸时长为30分钟或48小时） 以及无缺口与缺口（应力集中系数Kt分别为1.1、1.4、3.2）的扁平试样，测试工况包括： -> 空气环境（无氢氛围） -> 电化学渗氢环境（渗氢电流密度分别为5、20或50 mA/cm²） - 电化学渗氢测试： 包含无应力试样（渗氢电流密度分别为5、10、20、50和100 mA/cm²） 以及受拉伸载荷的试样（渗氢电流密度分别为5、20或50 mA/cm²）