Dataset for 'Pulsed field magnetisation of Y-Ba-Cu-O bulk superconductors fabricated by the infiltration growth technique'

Raw data obtained from the experiments carried out, are analysed and used for preparing some of the figures in the present manuscript are provided here. The data sets are provided in excel files, corresponding to respective figures. The files 'For figure-2(a)' and 'For figure-2(b)' contains columns with labels as trapped field magnitude, positions of X, and Y. These data are used to construct the 3-axis trapped field profiles as shown in Figures-2(a) and 2(b) in the paper. The files 'For Figure-3(b)' and 'For Figure-3(c), contains the columns indicating the magnetic field H (in the units of Oe) and Jc at respective temperatures of 85 K, 77 K, 65 K, 50 K, and 30 K as appropriate are provided in respective columns with columns as H and Jc at 85 K, for instance. These data are used for making X-Y plots representing the performance of 1-step BA-TSIG YBCO and 2-step BA-TSIG YBCO samples, as shown in figures 3(b) and 3(c). The file 'For figure-4(b)' contains columns with Temperature and Normalised magnetization data obtained from specimens extracted from different locations in the sample i.e. 1tb, 1td, 1tf, 1th, and 1tj. Details of these positions are indicated in figure-4(a) of the manuscript. The file 'For Figure-4(c)' contains data of applied field H (in Oe) and current density Jc (in A/cm2) for three different positions: 1td, 3td, and 5td i.e. along the a-growth region of the 2-step BA-TSIG YBCO sample. These data are plotted together to obtain figure-4(c). The file 'For Figure-4(d)' contains data of applied field H (in Oe) and current density Jc (in A/cm2) for five different positions: 1tb, 1td, 1tf, 1th, and 1tj i.e. along the c-growth region of the 2-step BA-TSIG YBCO sample. These data are plotted together to obtain figure-4(d).

本文提供了本研究实验过程中获取的原始数据，这些数据经分析处理后，用于绘制本文手稿中的部分图表。本数据集以Excel文件形式提供，与对应图表一一匹配。
文件'For figure-2(a)'与'For figure-2(b)'包含三列数据，表头分别为俘获场幅值、X轴位置与Y轴位置。上述数据用于构建论文中图2(a)及图2(b)所示的三轴俘获场分布。
文件'For Figure-3(b)'与'For Figure-3(c)'包含对应温度下的磁场H（单位：奥斯特（Oe））与临界电流密度Jc数据，涉及温度分别为85 K、77 K、65 K、50 K与30 K；各温度下的H与Jc分别单独成列，例如85 K组的列即为H与85 K下的Jc。上述数据用于绘制代表一步法BA-TSIG YBCO与两步法BA-TSIG YBCO样品性能的X-Y折线图，即论文中的图3(b)与图3(c)。
文件'For figure-4(b)'包含温度与归一化磁化强度数据，这些数据取自样品不同位置的试样，包括1tb、1td、1tf、1th与1tj。各采样位置的详细信息见本文手稿的图4(a)。
文件'For Figure-4(c)'包含三个不同采样位置（1td、3td与5td，即沿两步法BA-TSIG YBCO样品的a生长区域）的外加磁场H（单位：Oe）与临界电流密度Jc（单位：A/cm²）数据。将上述数据合并绘图即可得到图4(c)。
文件'For Figure-4(d)'包含五个不同采样位置（1tb、1td、1tf、1th与1tj，即沿两步法BA-TSIG YBCO样品的c生长区域）的外加磁场H（单位：Oe）与临界电流密度Jc（单位：A/cm²）数据。将上述数据合并绘图即可得到图4(d)。