Tensile SSRT on MS AHSS grade 1700 in presence of hydrogen

SSRT tensile curves obtained at room temperature on a commercial martensitic Advanced High Strength Steel grade 1700 in presence of a uniform initial hydrogen concentration. Hydrogen was introduced via eletrochemical charging prior the tensile test. The average hydrogen content in the specimen gauge length, reported in the file name, was measured after failure via hot extraction method. Financed by the European Union - NextGenerationEU (National Sustainable Mobility Center CN00000023, Italian Ministry of University and Research Decree n. 1033 - 17/06/2022, Spoke 11 - Innovative Materials & Lightweighting). The opinions expressed are those of the authors only and should not be considered as representative of the European Union or the European Commission’s official position. Neither the European Union nor the European Commission can be held responsible for them. Keywords: Spoke11 - CNMS MOST, Ferrous alloys

本数据集包含在室温条件下，针对商用马氏体先进高强度钢（Advanced High Strength Steel）1700级试样、于均匀初始氢浓度环境中测得的SSRT拉伸曲线。拉伸试验前，通过电化学充氢法向试样引入氢气。试样标距段的平均氢含量标注于文件名中，该含量在试样断裂后采用热萃取法测得。本研究由欧盟下一代欧盟（NextGenerationEU）项目资助，具体依托文件及单位包括：国家可持续流动中心CN00000023、意大利大学与研究部2022年6月17日第1033号政令、第11专题组——创新材料与轻量化技术。本研究仅代表作者个人观点，不应被视为欧盟或欧洲委员会的官方立场。欧盟及欧洲委员会不对本研究内容承担任何责任。关键词：第11专题组——CNMS MOST、铁合金