Uniaxial tensile test data for ALLOY 182 material at 288 °C

Data created at VTT, Finland in the scope of the NUGENIA MICRIN+ project on the development of an accelerated test method for stress corrosion cracking initiation. The work was concerned with SSRT/SCCI screening tests on tapered tensile specimens (both flat and cylindrical) to determine the SCCI threshold stress. The material investigated was Ni-based weld Alloy 182.