data on Wet oxidation of CrC-SiCr SiC coated C-SiC

Oxidation behavior of a Cr3Si-Cr7C3/SiC/SiC coated C/SiC composite was investigated in wet air at 700, 900 and 1300 ºC under 1 atm with a gas velocity of 3.0 cm s-1, and compared with that of a SiC/SiC/SiC coated C/SiC composite. XRD data of the coated samples before and after the wet oxidation for 10h; Data of Weight change of the coated 2D C/SiC composite during the wet oxidation and Flexural strength of the coated 2D C/SiC before and after the wet oxidation for 10h; Typical flexural stress-displacement data during loading of the coated 2D C/SiC before and after the wet oxidation for 10h.

本研究对Cr3Si-Cr7C3/SiC/SiC涂覆的C/SiC复合材料在700、900和1300°C的湿空气环境中，以1个大气压和3.0 cm/s的气流速度下进行的氧化行为进行了研究，并将其与SiC/SiC/SiC涂覆的C/SiC复合材料的氧化行为进行了比较。对涂层样品在10小时湿氧化前后的XRD数据进行了分析；记录了涂层二维C/SiC复合材料在湿氧化过程中的重量变化数据，以及涂层二维C/SiC在10小时湿氧化前后的弯曲强度；同时，还获得了涂层二维C/SiC在湿氧化前后10小时加载过程中的典型弯曲应力-位移数据。