Research data supporting "Optimisation of stacked, bulk high temperature superconductors for trapped-field magnet applications"

The dataset of Figure 4(1), 4(2), 4(3), 4(4), 4(5) and 4(6) contains the raw data of the trapped measurement correspondent to Figure 4(1), 4(2), 4(3), 4(4), 4(5) and 4(6). The trapped fields were measured using a rotating array consisting of 18 Hall probes at 1.5 mm above the surface of the sample. The fields signals were sent and recorded by Origin 8.5 (or later version), then the Origin generates contour maps for indicating the distribution of the fields. In this study, we use the contour maps to present the uniformity of the trapped fields. The dataset of Figure 8 thickness3.5 and Figure 8 thickness1.5 contains the raw data of the modelling results presented using Origin in Figure 8(a) and (b) where the thickness of the sample with Jc-B(1) is 1.5 mm & Jc-B(2) is 8.5 mm and the thickness of the sample with Jc-B(1) is 3.5 mm & Jc-B(2) is 6.5 mm respectively. The datasets of Figure 9, figure 10 and Figure 11 contain the raw data of the modelling results. Origin 8.5 (or later version) was used to draw the curves in Figure 9, figure 10 and Figure 11.