柔性铜铟镓硒薄膜太阳能组件的耐候性能测试数据集

本数据集在柔性铜铟镓硒组件的封装工艺和产品开发方面，通过柔性封装设计、封装工艺和电池组件可靠性的研究，记录了铜铟镓硒光伏组件的双85老化测试，紫外老化测试，户外光衰测试。封装后CIGS电池组件经1000h“双85”湿热试验后最大功率衰降仅为6.86%，户外光稳定测试衰减率为2.79%。

This dataset records the 85/85 aging test, ultraviolet aging test, and outdoor light-induced degradation test of copper indium gallium selenide (CIGS) photovoltaic modules. It is developed based on researches on flexible encapsulation design, encapsulation processes, and module reliability for the encapsulation process and product development of flexible CIGS solar modules. After undergoing a 1000-hour 85/85 damp heat test, the encapsulated CIGS solar modules show a maximum power degradation of only 6.86%, and the degradation rate measured in the outdoor light stability test is 2.79%.

搜集汇总

背景与挑战

背景概述

该数据集聚焦于柔性铜铟镓硒薄膜太阳能组件的耐候性能测试，涵盖了封装工艺和产品开发方面的研究。它记录了组件在双85老化、紫外老化和户外光衰测试中的表现，结果显示经过1000小时湿热试验后最大功率衰降仅为6.86%，户外光稳定测试衰减率为2.79%。